PE Talc Masterbatch (Blown-Film Grade)
Product Basics
Product Name
Transparent talc powder masterbatch for PE blown film
Referral Add Ratio
10%-30%
Product type
Functionally modified filler masterbatch
Carrier Material
Polyethylene PE
Talcum powder grain size
≤10μm
Density Range
1.05-1.20g/cm³
Recommended Processing Temperature
160-220℃
Applicable process
Blow film, injection molding, extrusion, particle extraction
Product Features and Benefits
- Specially designed for PE blown film process, excellent compatibility with polyethylene, uniform dispersion and no precipitation
- High purity transparent talc powder, very few impurities, regular sheet structure, little effect on film haze
- Flexible addition range, adjustable formula ratio according to mechanical and optical requirements
- Wide applicability, can meet the needs of blown film, injection molding, extrusion, grain extraction and other processing scenarios
- Origin factory produces independently, customized raw materials are supplied by large factories at home and abroad, and the quality is stable and controllable
Core Functional Features
Maintain excellent transparency
After special surface treatment and ultrafine processing, talc powder significantly reduces the light scattering effect. Adding 10-30% can still ensure high transparency of the film and meet the application scenarios that require high visual clarity.
After special surface treatment and ultrafine processing, talc powder significantly reduces the light scattering effect. Adding 10-30% can still ensure high transparency of the film and meet the application scenarios that require high visual clarity.
Synergistic Enhancement Mechanics
After addition, the film rigidity and tear strength can be improved while maintaining the toughness of the substrate; the unique layered structure can inhibit the heat shrinkage, improve the dimensional stability of the product, and reduce the shrinkage and deformation.
After addition, the film rigidity and tear strength can be improved while maintaining the toughness of the substrate; the unique layered structure can inhibit the heat shrinkage, improve the dimensional stability of the product, and reduce the shrinkage and deformation.
Suitable for a variety of processing techniques
Low friction coefficient improves melt fluidity, avoids material hanging and mold blocking in the blown film process; has good compatibility with PE, uniform dispersion and no reunion, and can be adapted to high-speed blown film production lines to reduce processing energy consumption.
Low friction coefficient improves melt fluidity, avoids material hanging and mold blocking in the blown film process; has good compatibility with PE, uniform dispersion and no reunion, and can be adapted to high-speed blown film production lines to reduce processing energy consumption.
Effectively reduce raw material costs
The 10-30% addition ratio can replace some PE resins, help reduce the cost of raw materials, do not affect the recyclability of products, and adapt to the needs of lightweight packaging.
The 10-30% addition ratio can replace some PE resins, help reduce the cost of raw materials, do not affect the recyclability of products, and adapt to the needs of lightweight packaging.
Scope of use and process compatibility
- Suitable substrates: LDPE, LLDPE, mLLDPE and other blown film grade polyethylene resins
- Applicable equipment: single/double layer coextrusion blowing machine
- Processing temperature: 160-220°C
- Recommendation: Recommended for use in combination with openers and antistatic agents
Tip: It is recommended to dynamically adjust the addition amount according to the film thickness, and the recommended addition amount of the film below 30μm is ≤ 15% to ensure transparency
TYPICAL APPLICATION FIELDS
High-performance food packaging film
It meets food safety standards, is used for bread bags, fresh tray film, daily chemical shrink packaging film, etc., and has high transparency and puncture resistance.
It meets food safety standards, is used for bread bags, fresh tray film, daily chemical shrink packaging film, etc., and has high transparency and puncture resistance.
Industrial protective film
It is used for the surface protection film of electronic products and the moisture-proof film of building materials. The high rigidity can resist transportation scratches, and the low heat shrinkage characteristics ensure the stability of the adhesion.
It is used for the surface protection film of electronic products and the moisture-proof film of building materials. The high rigidity can resist transportation scratches, and the low heat shrinkage characteristics ensure the stability of the adhesion.
Eco-friendly lightweight packaging film
For logistics container bags, ton bag lining film, through density optimization to achieve film thinning, still can maintain the original load-bearing capacity, to help reduce the cost of environmental protection.
For logistics container bags, ton bag lining film, through density optimization to achieve film thinning, still can maintain the original load-bearing capacity, to help reduce the cost of environmental protection.
Packaging & Logistics
25kg/composite bag 25kg/box or 1.35 tons/pallet, tray + wrapping film; national logistics can be dispatched for 2-3 days in the Pearl River Delta, 2-3 days in Jiangsu, Zhejiang and Shanghai, 3-4 days in remote areas (note: please contact the sales staff for specific packaging and arrival time); express delivery/vehicle/luggage can be supported.
Dongguan Qihao Plastic Co., Ltd.
Professional plastic additives, filling masterbatch manufacturers to support customized needs, welcome to consult and discuss
Professional plastic additives, filling masterbatch manufacturers to support customized needs, welcome to consult and discuss