PE Wax Flakes
.container { max-width: 850px; margin: 0 auto; font-family: 'Helvetica Neue', Arial, sans-serif; } .section-title { font-size: 24px; color: #1D1D1F; margin: 25px 0 15px; font-weight: 600; } .product-desc { color: #3A3A3C; font-size: 16px; line-height: 1.7; margin-bottom: 20px; } .feature-list { padding-left: 20px; margin: 15px 0; } .feature-list li { margin-bottom: 12px; color: #444446; list-style: none; } .feature-list li:before { content: "-"; margin-right: 8px; } .spec-table { width: 100%; border-collapse: separate; border-spacing: 0; border-radius: 8px; overflow: hidden; margin: 20px 0; } .spec-table th { background-color: #f5f5f7; color: #1D1D1F; text-align: left; padding: 12px 15px; font-size: 14px; font-weight: 500; border-bottom: 1px solid #e0e0e0; } .spec-table td { padding: 12px 15px; border-bottom: 1px solid #e0e0e0; color: #3A3A3C; font-size: 14px; line-height: 1.5; } .highlight-box { background-color: #f9f9fb; border-left: 4px solid #0071e3; padding: 15px; border-radius: 4px; margin: 20px 0; }PE wax flakes are special lubricating additives for plastic processing, offering excellent internal and external lubrication performance. They significantly improve melt flowability by reducing the cohesive force between resin molecules, reduce mold sticking, and enhance demolding effects. Their high molecular weight characteristics give them high melting point and low viscosity advantages, which can promote uniform dispersion of pigments/fillers and effectively improve the surface smoothness and gloss of products.
| Item | |
|---|---|
| Product form | Flake solid (irregular thin flakes) |
| Appearance | White translucent particles |
| Molscular weight | 2000-8000 |
| Melt temperature | 102-110℃ |
| Viscosity (140°C) | 200-600mPa·s |
| Acid value | ≤1mg KOH/g |
| Add Props | 0.1-1.0% (adjusted according to the resin system) |
- Increase fluidity - reduce melt viscosity by 20-40%, improve injection molding/extrusion efficiency
- Enhance demoldability - Reduce mold fouling, demolding force decreased by more than 30%
- Improve surface smoothness - eliminate flow marks and swirl patterns, reduce surface roughness by 15-25%
- Optimize dispersion performance - improve the uniformity of filler/pigment dispersion to over 95%
- Enhance thermal stability - can increase thermal stability time by 40-60% in PVC processing
- Improved wear resistance - The scratch resistance of the product surface is increased by 30-50%
- PVC Products:Pipes/Profiles/Sheets/Films/Artificial Leather (Addition 0.3-0.8%)
- Polyolefin Modification:PP/HDPE/LDPE color masterbatch and filled masterbatch (addition amount 1.0-3.0%)
- Engineering plasticProcessing lubrication for materials such as ABS/PC/PA (addition amount 0.2-0.5%)
- Rubber-plastic blending:TPE/TPR shoe materials and sealing parts (addition amount 0.5-1.5%)
- Hot melt adhesive:Reduce viscosity, increase open time
Standard packaging: 25kg/composite bag (with PE liner), 25kg/carton, whole pallet 1.35 tons (reinforced with stretch film)
Logistics Solution:
- Pearl River Delta area: dedicated logistics line, shipped today, delivered the next day
-Jiangsu, Zhejiang and Shanghai area: 2 days delivery
- Other regions: 3-4 days delivery (for specific timing, please consult customer service)
Supports express/freight/full truckload transportation, can handle nationwide logistics on your behalf