Universal Matting Masterbatch

Physical Properties TDS General Purpose Matt Masterbatch Q68

Physical Performance TDS General Purpose Matting Masterbatch Q68

Technical Parameters

Appearance: White semi-translucent granules

Appearance: White translucent particles

Melting point: 130-150℃

Melting Point: 130-150℃

Density: 1.2±0.1 g/cm³

Density: 1.2±0.1g/cm³

Volatile matter: ≤0.3%

Volatile Content: ≤0.3%

Recommended addition amount: 6%-8%

Recommended Dosage: 6%-8%

Product characteristics

Product Features

High-efficiency matting: Adding only 6%-8% can achieve a significant level of matte finish, eliminating unnecessary reflections on the plastic surface.

High-efficiency Matting: Only 6%-8% dosage can achieve significant matte grade, eliminate unnecessary reflection on plastic surface.

Wide range of applications: Compatible with processing methods such as film blowing, injection molding, extrusion, and pelletizing, and can be applied to various substrate systems such as PE, PP, and ABS.

Wide Application: Suitable for processing methods such as film blowing, injection molding, extrusion, granulation, and can be applied to various substrate systems such as PE, PP, ABS.

Good compatibility: Specifically designed for various engineering plastics, the white translucent version does not affect coloring and works well with pigments of all colors.

Good Compatibility: Designed for various engineering plastics, white translucent does not affect coloring, and works well with pigments of various colors.

Process stability: excellent dispersibility, not prone to white spots or agglomeration, wide processing window, and not likely to cause mold fouling.

Stable Process: Excellent dispersibility, not easy to produce white spots or agglomeration, wide processing window, not easy to cause mold scaling.

Texture quality: Provides products with a high-grade matte feel and visual uniformity, enhancing the added value of the product's appearance.

Product Texture: Endows products with high-grade frosted touch and visual uniformity, and improves the added value of product appearance.

Typical Performance Comparison Data Q68

Test item Test Item	Q68 Matte Masterbatch Q68 Matting MB	General Matte Masterbatch Common Matting MB	Competitor A Competitor A
Addition amount Dosage	6-8% 6-8%	12-15% 12-15%	8-10% 8-10%
60° gloss (black ABS substrate) 60°Gloss (Black ABS Substrate)	≤8GU ≤8GU	≤15GU ≤15GU	≤10GU ≤10GU
Dispersion Dispersibility	No white spots, no clumping No white spots, no agglomeration	Prone to white spots Prone to white spots	Small gathering A small amount of agglomeration
Mold fouling (continuous production for 8 hours) Mold Scaling (8h Continuous Production)	No build-up No scaling	Obvious scaling Obvious scaling	Slight scale buildup Slight scaling
Influence on mechanical properties Mechanical Property Impact	No effect No impact	Decrease by 10-15% Decrease by 10-15%	Decrease by 5-8% Decrease by 5-8%

Note: The above data are standard laboratory test results; actual effects may vary slightly due to process parameters.

Note: The above data are standard laboratory test results, actual effect varies slightly due to process parameters

Typical Application Features Q68

Typical Application Function Q68

Applicable substrates: PE, PP, ABS, PS, PC, PA and other general and engineering plastics

Applicable Substrates: PE, PP, ABS, PS, PC, PA and other general and engineering plastics

Applicable processing technologies: blow molding, injection molding, extrusion, pelletizing, calendaring, etc.

Applicable Processing Technology: Film blowing, injection molding, extrusion, granulation, casting, etc.

Typical Application Products

Consumer electronics casing

Consumer electronics shell

Car interior parts

Automotive interior parts

Matte film, packaging bags

Matte film, packaging bag

Household daily necessities, toys

Building Material Decorative Profiles

Building material decoration profiles

Methods Used

Usage Method

Mix this product evenly with the base resin in the specified proportion, and it can be processed directly.

Mix the product with base resin in proportion evenly and process directly

No need to change the original processing parameters

No need to change original processing parameters

Notice

Precautions

After opening, please seal and store to avoid moisture.

Seal and store after opening if not used up to avoid moisture

It is recommended to conduct a small test before use to determine the optimal amount to add.

It is recommended to conduct a small test before use to determine the optimal dosage